| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Novalloy-B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ulrofL_Novalloy-B-B1300-B1300F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-B B1300, B1300F is an Acrylonitrile Butadiene Styrene + PBT (ABS+PBT) material. It is available in Asia Pacific. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.50 to 0.80 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 38.0 | MPa | ISO 527-2 |
| Flexural Modulus | 1800 | MPa | ISO 178 |
| Flexural Stress | 57.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 6.40 mm) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 100 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 5.00 to 20.0 | MPa | |
| Screw Speed | 50 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Syncure™ System S100NA | PolyOne Corporation | XLPE | Syncure™ |
| TAROMID B 280 G2 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| Celstran® +PP-GF30-05CN05/10 | Celanese Corporation | PP Copolymer | Celstran® |
| DIALAC® E359B | UMG ABS, Ltd. | ASA+PMMA | DIALAC® |
| Polyrocks 666(f1) | Polyrocks Chemical Co., Ltd | PP, Unspecified | Polyrocks |