Syncure™ S1027A
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Syncure™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ulkEp8_Syncure-S1027A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Moisture cross-linked polyethylene composite material. Base resin composition, used in the Syncure system of Plivan. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ASTM D1505 |
| Apparent Density 1 | 0.53 | g/cm³ | Internal method |
| Melt Mass-Flow Rate (MFR) 2(190°C/2.16 kg) | 0.73 | g/10 min | ASTM D1238 |
| Gel Content 3 | 75 | % | ASTM D2765 |
| Appearance | Particles/cubes | ASTM D2090 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Tensile strength retention rate 4(168°C, 1.91 mm) | 85 | % | |
| Elongation retention rate 5(168°C, 1.91 mm) | 80 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation 6(131°C) | 3.0 | % | UL 1581 |
| Thermal creep elongation 7 | 35 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 8(Break) | 17.9 | MPa | ASTM D638 |
| Tensile Elongation 9(Break) | 450 | % | ASTM D638 |
| Additional Information |
|---|
| 张力、炉内老化值基于100 phr S1027A / 20 phr V0022G系统测量得出。变形值、热蠕变和凝胶值基于95 phr S1027A / 5 phr S1000B系统测量得出；全部在90摄氏度的水中硫化6小时。颗粒外观为 1/8"圆柱状。 |
| Note Message | |
|---|---|
| 1 . | Geon® 1169 |
| 2 . | Procedure A |
| 3 . | Cross-linked PE, Method B (Non-Arbitration Test) |
| 4 . | 168 hours, UL standard |
| 5 . | 168 hours, UL standard |
| 6 . | 500g,1 hour |
| 7 . | SYV-40 |
| 8 . | Type 4, 510mm/min |
| 9 . | Type 4, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sorona® FG3301 NC010 | DuPont Performance Polymers | PTT | Sorona® |
| Nypol® PA A3 T15 CNZ0093 NR331 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Bynel® 41E687 | DuPont Packaging & Industrial Polymers | LLDPE | Bynel® |
| CYROLITE® Med 2 | Evonik Cyro LLC | Acrylic (PMMA) | CYROLITE® |
| Luxus PP 16077 | Luxus Limited | PP, Unspecified | Luxus PP |