Laril 13 G/30-V1
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laril |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ulYxRk_Laril-13-G-30-V1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Modified Polyphenylene Oxyde (PPOm). Glass fibres. UL94 V-1 classified, halogens and red phosphorous free. Product UL certified. High dimensional stability. Good thermal resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.45 to 0.65 | % | |
| Flow : 2.00 mm | 0.35 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 8600 | MPa | |
| 60°C | 7800 | MPa | |
| 90°C | 6600 | MPa | |
| 120°C | 4500 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 120°C | 40.0 | MPa | |
| Break, 23°C | 95.0 | MPa | |
| Break, 60°C | 80.0 | MPa | |
| Break, 90°C | 65.0 | MPa | |
| Break, 120°C | 40.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 120°C | 1.0 | % | |
| Break, 23°C | 1.5 | % | |
| Break, 60°C | 1.5 | % | |
| Break, 90°C | 1.8 | % | |
| Break, 120°C | 2.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 20 | kJ/m² | |
| 23°C | 18 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 95 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 115 | °C | |
| Vicat Softening Temperature | 135 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-1 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Oxygen Index | 31 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxiglas® MG515 | Maxiglas Corporation | Acrylic (PMMA) | Maxiglas® |
| Sarlink® TPE EE-2245N | Teknor Apex Company | TPE | Sarlink® TPE |
| Spartech Polycom SC14-1090 | Spartech Polycom | Nylon 66 | Spartech |
| Alcryn® 2080 BK | Advanced Polymer Alloys | MPR | Alcryn® |
| LNP™ THERMOCOMP™ WF006 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |