LNP™ VERTON™ RV008ES compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ulSRvc_LNPVERTONRV008EScompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON RV008ES is a compound based on Nylon 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. Also known as: LNP* VERTON* Compound RF-7008 EM HS Product reorder name: RV008ES |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.48 | g/cm³ | ASTM D792 |
| -- | 1.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.20 - 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.69 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.29 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.70 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13800 | MPa | ASTM D638 |
| -- | 13200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 214 | MPa | ASTM D638 |
| Yield | 207 | MPa | ISO 527-2 |
| Fracture | 214 | MPa | ASTM D638 |
| Fracture | 206 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.9 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2 |
| Fracture | 1.9 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 11700 | MPa | ASTM D790 |
| -- | 12000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 303 | MPa | ASTM D790 |
| -- | 301 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 210 | J/m | ASTM D256 |
| 23°C 2 | 21 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 3 | 70 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 8.60 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 253 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 255 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 248 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 250 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 6.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 2.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 288 - 299 | °C | |
| Processing (Melt) Temp | 288 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLLAMID A 2700 - A 2730 FV 35 | Krisoll Resinas Plásticas Ltda. | Nylon 66 | SOLLAMID |
| Moplen HP515M | LyondellBasell Industries | PP Homopolymer | Moplen |
| AIE PP 80T10 | Asia International Enterprise (Hong Kong) Limited | PP, Unspecified | AIE PP |
| ESPOLEX 821 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |
| HiFill® ABS WM20 | Techmer Engineered Solutions | ABS | HiFill® |