Order Products : sales@su-jiao.com
Polylink Power Cable PP 408/401
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Polylink Polymers (India) Ltd. |
| Trademark: | Polylink Power Cable |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ukeQA0_Polylink-Power-Cable-PP-408-401.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A silane grafted crosslinkable polyethylene compound, curable by exposure to moisture, for insulation of power cables and possessing excellent extrudability at high out put rate. PP 408 is based on a high molecular weight polymer and has melt index in the range of 0.5 to 0.8. It has especially developed for low voltage cable insulation and for sheathing purpose. DESCRIPTION : This compound utilizes the system for cross - linking of polyethylene developed by DOW Corning and known as Sioplas. It is a two component system comprising a silylated ethylene polymer known as the graft copolymer PP 408 , and a master batch PP 401 containing a cross - linking catalyst. The two materials normally used in the ratio of 95 parts graft to 5 parts catalyst master batch. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 18.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 550 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 168 hr) | 10 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air (135°C, 168 hr) | 15 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811 | ||
| Elongation Under Load : 200°C | 100 | % | IEC 60811 |
| Permanent Elongation after Cooling : 200°C | 5.0 | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Power factor (23°C) 2 | 4.00E-4 | IEC 250 | |
| Volume Resistivity (20°C) | 2.4E+16 | ohms·cm | IEC 60502 |
| Dielectric Strength | 25 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 2.30 | IEC 60250 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 180 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Cylinder Zone 5 Temp. | 200 | °C | |
| Die Temperature | 210 | °C |
| Extrusion instructions |
|---|
| Screw water temperature : 60 to70°CScreens : 30,100,30(mesh apertures per linear inch)L/D Ratio: 20Compression: 3:0:1 |
| Note Message | |
|---|---|
| 1 . | 15 min, 0.2 N/mm² |
| 2 . | 50 Hz |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra POM | ResMart | Acetal (POM) Copolymer | ResMart Ultra |
| AKROTEK® PK-VM GF 30 natural (4706) | AKRO-PLASTIC GmbH | PK-Aliphatic | AKROTEK® |
| Di-Pak™ E-4541-3 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| LNP™ THERMOCOMP™ Lexan_JK500 compound | SABIC Innovative Plastics | PC+ABS | LNP™ THERMOCOMP™ |
| MAXATEL® AH100ST-NC010 | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | MAXATEL® |