INEOS PP N00N-00
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uk2KPr_INEOS-PP-N00N-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| N00N-00 is a fractional melt flow rate high impact copolymer polypropylene specifically designed for non-pressure structured wall pipe but can also be used in other extrusion applications requiring high melt strength and high stiffness. It offers a superior balance of stiffness and impact strength as compared to competitive impact copolymers of similar melt flow rate. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.910 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.35 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 33.9 | MPa | |
| Break | 26.2 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 7.9 | % | |
| Break | 120 | % | |
| Flexural Modulus - 1% Secant | 1790 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 85 | J/m | |
| 23°C | 950 | J/m | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C | 8.20 | kJ/m² | |
| 23°C | 93.4 | kJ/m² | |
| Instrumented Impact, Ductility | ASTM D3763 | ||
| -20°C | Ductile | ||
| 23°C | Ductile |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 114 | °C | |
| 1.8 MPa, Unannealed | 60.0 | °C | |
| Vicat Softening Temperature | 159 | °C | ASTM D1525 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 78 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMORUN® QT85MA | Mitsubishi Chemical Corporation | TPO (POE) | THERMORUN® |
| Koylene ADL AS160N | Reliance Industries Limited | PP Homopolymer | Koylene ADL |
| ICORENE® 1314 | ICO Polymers EMEA, A Division of A. Schulman | LMDPE | ICORENE® |
| Karina COMP. PVC CRYSTAL -E 57/201-D-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYFLON™ D-210 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |