LNP* THERMOCOMP* OF008AE is a compound based on PPS - Branched resin containing 40% Glass Fiber. Added feature of this grade is: Easy Molding. Also known as: LNP* THERMOCOMP* Compound OF-1008 EM Product reorder name: OF008AE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.36 | % | |
| Across Flow : 24 hr | 1.2 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.21 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 17000 | MPa | ASTM D638 |
| -- | 16300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 133 | MPa | ASTM D638 |
| Break | 128 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 0.90 | % | ASTM D638 |
| Break | 0.90 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 16100 | MPa | ASTM D790 |
| -- 5 | 15500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 197 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 205 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 90 | J/m | ASTM D256 |
| 23°C 7 | 8.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 300 | J/m | ASTM D4812 |
| 23°C 8 | 19 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 4.16 | J | ASTM D3763 |
| -- | 2.08 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 280 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 277 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 271 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 366 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 3.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xydar® G-930 | Solvay Specialty Polymers | LCP | Xydar® |
| Cheng Yu VH825 | Cheng Yu Plastic Company Limited | ABS | Cheng Yu |
| Laticonther 52/35 CP1/45 | LATI S.p.A. | PP Homopolymer | Laticonther |
| KumhoSunny PBT HEB4010 | Shanghai KumhoSunny Plastics Co., Ltd. | PBT | KumhoSunny PBT |
| Karina IVORY PVC COMPOUND 751-35/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |