Marlex® 5626
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | Marlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uhAmdr_Marlex5626.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
This low density polyethylene is tailored for blown film applications that require:
Typical blown film applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.65 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 51 µm, blown film | 180 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm, blown film | 210 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 25.0 | MPa | ASTM D882 |
| TD : Broken, 51 µm, blown film | 24.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 230 | % | ASTM D882 |
| TD : Broken, 51 µm, blown film | 540 | % | ASTM D882 |
| Oxygen Permeability (51 µm, Blown Film) | 210 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (51 µm, Blown Film) | 0.47 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Dart Drop Test - Blown Film (50.8 µm) | 42.5 | kN/m | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 50.8 µm | 37.1 | kN/m | ASTM D1922 |
| TD : 50.8 µm | 41.7 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 114 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 50.8 µm, Blown Film) | 82 | ASTM D2457 | |
| Haze (50.8 µm, Blown Film) | 10 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC PNC87-5-8135 | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| VINIKA® CE55EG | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Delta N66R-4G30 | Delta Polymers | Nylon 66 | Delta |
| Karina IVORY PVC COMPOUND 105905-35/ 1-BY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ LC003E compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |