Leona™ 1402SH
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uh3OLo_Leona-1402SH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ 1402SH is a Polyamide 66 (Nylon 66) product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ 1402SH include automotive, electrical/electronic applications, engineering/industrial parts and wire & cable. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 1.3 to 2.0 | -- | % | Internal Method |
| Water Absorption | ||||
| Saturation, 23°C | -- | 2.5 | % | |
| Equilibrium, 23°C, 50% RH | -- | 2.5 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785, ISO 2039-2 | |||
| M-Scale | 80 | 55 | ||
| R-Scale | 120 | 108 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | 1100 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Yield, 23°C | 82.0 | 48.0 | MPa | ISO 527-2 |
| -- | 79.0 | 55.0 | MPa | ASTM D638 |
| Tensile Strain | ||||
| Yield, 23°C | 4.5 | 25 | % | ISO 527-2 |
| Break | 50 | 270 | % | ASTM D638 |
| Break, 23°C | -- | > 50 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 2800 | 1000 | MPa | ASTM D790 |
| 23°C | 2600 | 900 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 118 | 50.0 | MPa | ASTM D790 |
| 23°C | 111 | 38.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | -- | 7.00 | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179 | |
| Notched Izod Impact | 39 | 200 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 230 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 162 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 62.0 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 8.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | -- | J/kg/°C | |
| Thermal Conductivity | 0.20 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 20 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.00 mm) | 525 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | V-2 | -- | UL 94 | |
| Oxygen Index | 26 | -- | % | ASTM D2863 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® MR340 42H-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Aarolene® AVPS GP 100-1 | Aaron Industries Corp. | PS (GPPS) | Aarolene® |
| Adell Polyamide AB-34 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| PEEK-OPTIMA® Granular | Invibio Inc. | PEEK | PEEK-OPTIMA® |
| Plexiglas® 8N | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |