Ultrason® P 3010
| Category: | PPSU , Polyphenylsulfone |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultrason® P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ugMCt9_Ultrason-P-3010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultrason P 3010 is an unfilled, flame retardant, higher viscosity injection molding PPSU grade, with improved chemical resistance. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/10.0 kg) | 35.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.0 | % | |
| Flow | 0.90 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.2 | % | |
| Equilibrium, 23°C, 50% RH | 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 124 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2270 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 74.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 7.8 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 25 | kJ/m² | |
| 23°C | 75 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180 | ||
| -30°C | 25 | kJ/m² | |
| 23°C | 55 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 198 | °C | ISO 75-2/A |
| CLTE - Flow | 5.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 44 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.80 | ||
| 1 MHz | 3.70 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.7E-3 | ||
| 1 MHz | 8.9E-3 | ||
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.00 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VECTOR® 4211 | Dexco Polymers LP | SIS | VECTOR® |
| AME™ 1001 INF | Ashland Performance Materials | Vinyl Ester | AME™ |
| Exceed™ 1018KB | ExxonMobil Chemical | mPE | Exceed™ |
| Hostaform® S 9362 XAP² ™ | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Lustran® ABS 682 | INEOS ABS (USA) | ABS | Lustran® ABS |