SCHULAMID® 6 GF 15 FR 4 K1681 DEEP BLACK 96.8086
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ufyEqh_SCHULAMID-6-GF-15-FR-4-K1681-DEEP-BLACK-96-8086.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% glass fibre reinforced flame-retardant Polyamide 6 grade without PBDE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183/A |
| Viscosity Number | 136 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break, 23°C) | 123 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.2 | kJ/m² | |
| 23°C | 6.6 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 44 | kJ/m² | |
| 23°C | 52 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 213 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 197 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 213 | °C | ISO 306/A50 |
| -- | 205 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 1 | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.400 mm | V-2 | ||
| 0.800 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.380 mm | 800 | °C | |
| 0.750 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.380 mm | 825 | °C | |
| 0.750 mm | 900 | °C | |
| 1.50 mm | 900 | °C | |
| 3.00 mm | 900 | °C | |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | < 240 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 80.0 to 140 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Classe 3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A HS 372 M NER | Radici Plastics | Nylon 66 | Radilon® |
| SABIC® HDPE F04660 (Blow moulding) | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| VENYL SE038L | AD majoris | Nylon 6 | VENYL |
| ChronoFlex® AL 65D | CardioTech International, Inc. | PUR, Unspecified | ChronoFlex® |
| Favorite LL051 | Favorite Plastics | LDPE+LLDPE | Favorite |