Generic TPO
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ufpkD5_Generic-TPO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TPO This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.891 - 1.11 | g/cm³ | ASTM D792 |
| 23°C | 0.897 - 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 0.50 - 27 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.80 - 30 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 12.9 - 21.7 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.99 - 1.7 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 36 - 94 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1000 - 2950 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 14.6 - 26.6 | MPa | ASTM D638 |
| Yield, 23°C | 15.0 - 33.8 | MPa | ISO 527-2 |
| Fracture, 23°C | 12.9 - 18.4 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield, 23°C | 2.8 - 10 | % | ISO 527-2 |
| Fracture, 23°C | 47 - 510 | % | ASTM D638 |
| Fracture, 23°C | 4.0 - 63 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 172 - 2300 | MPa | ASTM D790 |
| 23°C | 870 - 1900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.4 - 7.5 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 7.0 - 510 | J/m | ASTM D256 |
| 23°C | 3.2 - 54 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 15.7 - 20.8 | J | ASTM D3763 |
| Dart Drop Impact (23°C) | 16.2 - 30.5 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 90.4 - 140 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 67.0 - 121 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 46.1 - 65.5 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 98.9 - 138 | °C | ISO 306 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 74.3 - 79.7 | °C | |
| Drying Time | 1.0 - 3.5 | hr | |
| Rear Temperature | 195 - 213 | °C | |
| Middle Temperature | 200 - 215 | °C | |
| Front Temperature | 204 - 221 | °C | |
| Nozzle Temperature | 207 - 220 | °C | |
| Processing (Melt) Temp | 213 - 215 | °C | |
| Mold Temperature | 29.4 - 54.4 | °C | |
| Back Pressure | 0.517 - 44.1 | MPa | |
| Clamp Tonnage | 4.1 - 4.5 | kN/cm² |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPOThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safron® R701-40RNA | Safripol (PTY) LTD | PP Random Copolymer | Safron® |
| VESTAKEEP® Film 0FH80 | Evonik Industries AG | PEEK | VESTAKEEP® Film |
| ALTECH® PP-H A 3020/100 GB20 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| LNP™ STAT-KON™ KX96321 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ STAT-KON™ |
| ESTOPLAST XU 150HFNN02 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |