Rilsan® BESNO MED
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uctVgI_Rilsan-BESNO-MED.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® BESNO MED is a polyamide produced from a renewable source. This grade dedicated to extrusion offers the highest quality and it is specifically designed to meet the stringent requirements of the medical applications such as minimally invasive devices. Upon request letters regarding USP Class VI compliance can be provided. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 76 | ||
| Shore D, 15 sec | 71 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 40.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 1130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 186 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA11, E, 22-010 | ISO 1874 | |
| Renewable Carbon Conent | 100 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.0 to 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Melt Temperature | 230 to 280 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 145 | Salflex Polymers Ltd. | TPO (POE) | Salflex |
| RTP 102 CC | RTP Company | PP, Unspecified | RTP |
| Shin-Etsu RTV KE-3417 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| Cellophane™ 335WSB | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Sylvin 8200-80 Grey 9586 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |