DOWLEX™ 2064G
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ucEOd9_DOWLEX-2064G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ 2064G Polyethyelene Resin is cast extrusion linear low density polyethylene resin grade suitable for artificial turf yarns including slit tapes and monofilaments. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.935 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Resistance | 10.3 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 324 | J/cm³ | ASTM D882 |
| TD | 308 | J/cm³ | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 16.9 | MPa | ASTM D882 |
| TD : Yield | 17.6 | MPa | ASTM D882 |
| MD : Fracture | 59.2 | MPa | ASTM D882 |
| TD : Fracture | 39.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 620 | % | ASTM D882 |
| TD : Fracture | 750 | % | ASTM D882 |
| Dart Drop Impact | 57 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD | 83 | g | ASTM D1922 |
| TD | 290 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 119 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 125 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 90 | ASTM D2457 | |
| Haze | 2.6 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 274 | °C |
| Extrusion instructions |
|---|
| Fabrication Conditions For Cast Film: EGAN/Davis-Standard 5 layer cast line Melt Temperature: 525°F (274°C) Chill Roll (primary/secondary) Temperature: 70°F (21°C) Line Speed: 600 fpm (183m/min) Die Width: 24in. (520mm) Die Gap: 25mil (0.6mm) |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer SG7 | Shanghai Potomer International Trade Co., Ltd. | PVC, Rigid | Shanghai Potomer |
| SILVER® SA-3154 | Guangdong Silver Age Sci & Tech. Co., Ltd | TPE | SILVER® |
| Braskem PP CP 195 | Braskem | PP Impact Copolymer | Braskem PP |
| FHR Polypropylene AP5206-HN | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Grilamid® XE 4129 black 9020 | EMS-GRIVORY | Nylon 610 | Grilamid® |