Edgetek™ PA-45GF/000 BK005
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ubirW6_Edgetek-PA-45GF-000-BK005.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Edgetek™PA-45GF/000 BK005 is a polyamide product containing a 45% glass fiber reinforced material. It can be processed by injection molding and is available in the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 160 | MPa | ASTM D638 |
| Flexural Modulus 2 | 11000 | MPa | ASTM D790 |
| Flexural Strength 3 | 300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 280 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 120 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 320 - 340 | °C | |
| Middle Temperature | 320 - 340 | °C | |
| Front Temperature | 320 - 340 | °C | |
| Mold Temperature | 120 - 135 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Akulon® K224-PG8 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| EPO-TEK® H70E-2 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Huafon JF-S-DR35 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Kuraray Poval® PVA 236 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| LEXAN™ CFR9111 resin | SABIC Innovative Plastics | PC | LEXAN™ |