PLUSTEK PA340S4
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ub2gSq_PLUSTEK-PA340S4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% GLASS-BEADS REINFORCED POLYAMIDE 66 FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 1.5 to 2.0 | % | ASTM D955 |
| -- | 1.5 to 2.0 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 5.8 | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 76.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 to 4.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 4050 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 120 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 40 | J/m | ASTM D256 |
| 23°C | 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 190 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 256 | °C | ISO 11357-3, ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 80 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.80 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Flammability Index | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 270 to 280 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 285 to 310 | °C | |
| Mold Temperature | 65.0 to 110 | °C | |
| Injection Pressure | 70.0 to 125 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 to 85.0 | MPa | |
| Back Pressure | 0.350 to 0.700 | MPa | |
| Screw Speed | 60 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ RDU100 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| ACCULOY™ POL062L | ACLO Compounders Inc. | PC+PET | ACCULOY™ |
| ACRYLITE® Sheet LED Sign Grade | Evonik Cyro LLC | Acrylic, Unspecified | ACRYLITE® Sheet |
| Geon™ Vinyl Flexible 90043 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Infino TX-0520H | LOTTE ADVANCED MATERIALS CO., LTD. | MABS | Infino |