LEXAN™ FL900S resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uYyr0Q_LEXAN-FL900S-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Foamable Lexan* FL900S polycarbonate resin is an ideal choice for structural components where load bearing capability at elevated temperature is a key requirement. It exhibits outstanding inpact strength, high heat resistance, flexural characteristics, creep resistance and processa- bility. In addition, it is an excellent alternative to metal for large components with broad application potential in the appliance, automotive, telecommunications, material, handling and business machine industries. The material contains 5% glass fiber and combines regidity, impact strength and toughness with UL 94 V-0 and 5V listings. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 1 | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | |||
| 24 hr | 0.15 | % | ASTM D570 |
| Saturation, 23°C | 0.35 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 42.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 2400 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Impact | 50.0 | J | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 128 | °C | ISO 75-2/Af |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 75°C | Pass | ||
| 125°C | Pass | ||
| CLTE - Flow (23 to 80°C) | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 280 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.15 | W/m/K | ISO 8302 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | ASTM D149 | ||
| 0.800 mm, in Oil | 35 | kV/mm | |
| 1.60 mm, in Oil | 27 | kV/mm | |
| 3.20 mm, in Oil | 17 | kV/mm | |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 2.41 | ||
| 1 MHz | 2.30 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 2.9E-3 | ||
| 1 MHz | 0.010 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | V-0 | ||
| 5.00 mm | 5VA | ||
| Oxygen Index | 35 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 5.0 | % | ASTM D229 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 265 to 295 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 290 to 320 | °C | |
| Nozzle Temperature | 290 to 320 | °C | |
| Processing (Melt) Temp | 290 to 320 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CP PRYME® Polypropylene PPC100ZNA/3.5I-12M NAT | Chase Plastics Services Inc. | PP Impact Copolymer | CP PRYME® Polypropylene |
| Hostacom EP Q 40 RN/6 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| LIHAN® A7010 | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |
| Plaslube® PA6/6 GF13 ML2 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| LUVOCOM® 94-8839/ES | LEHVOSS Group | LDPE | LUVOCOM® |