Honeywell PCTFE P900TR

Category:	PCTFE , Polychlorotrifluoroethylene
Manufacturer:	Honeywell
Trademark:	Honeywell PCTFE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	uX6fiT_Honeywell-PCTFE-P900TR.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Honeywell PCTFE P-Series TR film is a poly-chlor-tri-fluoroethylene homopolymer, high performance barrier film for industrial and electronics applications. It provides outstanding water vapor barrier and excellent chemical resistance.

General Information
Features	Good chemical resistance Barrier resin
Uses	Films
Forms	Films

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.10	g/cm³	ASTM D792

Films	Nominal Value	Unit	Test Method
secant modulus			ASTM D882
MD	1380	MPa	ASTM D882
TD	1290	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Fracture	115	MPa	ASTM D882
TD : Fracture	51.0	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Fracture	100	%	ASTM D882
TD : Fracture	250	%	ASTM D882
Water Vapor Transmission	0.26	g/m²/24 hr	ASTM E96

Thermal	Nominal Value	Unit	Test Method
Peak Crystallization Temperature (DSC)	211	°C	ASTM D3418

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	100	%	ASTM D2863

Optical	Nominal Value	Unit	Test Method
Haze	< 1.0	%	ASTM D1003

Additional Information
Yield: 14595 in²/lbTensile Strength @ Break, ASTM D 882, MD: 11000 to 20500 psiTensile Strength @ Break, ASTM D 882, TD: 6400 to 8400 psiElongation @ Break, ASTM 882, MD: 70 to 130%Elongation @ Break, ASTM 882, TD: 200 to 300%Secant Modulus, ASTM D 882, MD: 175000 to 225000 psiSecant Modulus, ASTM D 882, TD: 170000 to 205000 psiGraves Tear (initial), ASTM D 1004, MD: 325 to 375 g/milGraves Tear (initial), ASTM D 1004, TD: 275 to 325 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: -8 to -13% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: +8 to +15% shrinkageFlammability: Non-flammable

Additional Information

Yield: 14595 in²/lbTensile Strength @ Break, ASTM D 882, MD: 11000 to 20500 psiTensile Strength @ Break, ASTM D 882, TD: 6400 to 8400 psiElongation @ Break, ASTM 882, MD: 70 to 130%Elongation @ Break, ASTM 882, TD: 200 to 300%Secant Modulus, ASTM D 882, MD: 175000 to 225000 psiSecant Modulus, ASTM D 882, TD: 170000 to 205000 psiGraves Tear (initial), ASTM D 1004, MD: 325 to 375 g/milGraves Tear (initial), ASTM D 1004, TD: 275 to 325 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: -8 to -13% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: +8 to +15% shrinkageFlammability: Non-flammable

Resin Grade	Manufacturer	Category	Trademark
Telcar® TL-2450F	Teknor Apex Company	TPE	Telcar®
CERTENE鈩?LLHF-0826A	Muehlstein	LLDPE	CERTENE™
Fixmaster Epoxy Corrosion Coating	Loctite®	Epoxy	Fixmaster
Jam PE 60518	Jam Petrochemical Company	HDPE	Jam PE
Sumiliteresin® PR-51820	SBHPP	Phenolic	Sumiliteresin®