| 32 mol% Ethylene Vinyl Alcohol Copolymer |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 1.7 | g/10 min | |
| 210°C/2.16 kg | 4.2 | g/10 min | |
| Ethylene Content | 32.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 86 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 17 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability | ISO 14663-2 | ||
| 20°C, 65% RH | 7.9E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.034 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 1(40°C, 90% RH) | 1.8 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 2.0 | kJ/m² | ISO 179/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 56.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 162 | °C | ISO 306 |
| Melting Temperature | 183 | °C | ISO 11357 |
| Peak Crystallization Temperature | 156 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® F02-081A-10C | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| APICAL 200AV | Kaneka Corporation | PI, TS | APICAL |
| ExxonMobil™ PP8255E1 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| ESTOPLAST EP 4140GY01 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| POCAN® KU 2-7604 000000 | LANXESS Corporation | PC+PBT | POCAN® |