LNP™ THERMOCOMP™ EC005R compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uVNCkC_LNP-THERMOCOMP-EC005R-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP EC005R is a compound based on Polyetherimide resin containing 25% Carbon Fiber. Added features include: Mold Release, Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound EC-1005 MR Product reorder name: EC005R |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0E-3 to 3.0E-3 | % | |
| Across Flow : 24 hr | 4.0E-3 to 6.0E-3 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.18 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.18 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 42000 | MPa | ASTM D638 |
| -- | 22900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 132 | MPa | ASTM D638 |
| Yield | 83.0 | MPa | ISO 527-2/5 |
| Break 3 | 201 | MPa | ASTM D638 |
| Break | 179 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 0.0 | % | ISO 527-2/5 |
| Break 4 | 0.72 | % | ASTM D638 |
| Break | 1.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 19100 | MPa | ASTM D790 |
| -- 6 | 18600 | MPa | ISO 178 |
| Flexural Strength 7(Break, 50.0 mm Span) | 276 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D256 |
| 23°C 8 | 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 520 | J/m | ASTM D4812 |
| 23°C 9 | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 214 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 217 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 207 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 210 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 1.9E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 2.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 354 to 366 | °C | |
| Front Temperature | 366 to 377 | °C | |
| Processing (Melt) Temp | 360 to 366 | °C | |
| Mold Temperature | 121 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE EE-2272B BLK | Teknor Apex Company | TPE | Sarlink® TPE |
| WanBlend® WHT-THF9465T2 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | WanBlend® |
| Bayfill® 382 (53.2:100) | Covestro - PUR | PUR-MDI | Bayfill® |
| Grilamid® L 20H FWA black 9225 | EMS-GRIVORY | Nylon 12 | Grilamid® |
| LNP™ THERMOCOMP™ 9X98071 compound | SABIC Innovative Plastics Europe | Nylon 610 | LNP™ THERMOCOMP™ |