Plexiglas® V052i
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uUhzSG_Plexiglas-V052i.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plexiglas® V052i is a lightly impact modified thermoplastic acrylic resin formulated for injection molding. It is characterized by its chemical and heat resistance as well a good melt flow and excellent mold release properties. It is a tougher resin than Plexiglas® V052 allowing improved fabrication. It offers an excellent balance between melt flow and increased resistance to breakage, while providing weatherability superior to that provided by other high-impact plastics. Moldflow simulation data is available. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 84 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2830 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 63.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 22 | % | ASTM D638 |
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 21 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 103 | °C | |
| 1.8 MPa, Annealed | 97.2 | °C | |
| Vicat Softening Temperature | |||
| -- | 110 | °C | ASTM D1525 2 |
| -- | 102 | °C | ASTM D1525 3 |
| Thermal Conductivity | 0.19 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 4 | 1.490 | ASTM D542 | |
| Transmittance (3180 µm) | 91.0 | % | ASTM D1003 |
| Haze (3180 µm) | < 1.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ASTM Classification | PMMA 0211V3 | ASTM D788 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 50 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 216 | °C | |
| Middle Temperature | 221 | °C | |
| Front Temperature | 227 | °C | |
| Nozzle Temperature | 221 | °C | |
| Processing (Melt) Temp | < 271 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 to 2.5:1.0 | ||
| Vent Depth | 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | Annealing cycle: 4hrs @ 176°F |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| 4 . | ND @ 72°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EPS30R | Shazand (Arak) Petrochemical Corporation | PP Copolymer | Moplen |
| Unichem 6574 | Colorite Polymers | PVC, Unspecified | Unichem |
| LIHAN® A601 | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |
| LOXIM 600 00 HB | LOXIM Industries Private Limited | PC+PBT | LOXIM |
| Rotuba CAB B9024 (5% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |