Generic SAN - Glass Fiber
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uTfx4M_Generic-SAN---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic SAN - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.09 - 1.41 | g/cm³ | ASTM D792 |
| 23°C | 1.15 - 1.36 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 2.8 - 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.10 - 0.30 | % | ASTM D955 |
| 23°C | 0.20 - 0.31 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.12 - 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 89 - 125 | ASTM D785 | |
| 23°C | 86 - 125 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 4580 - 13300 | MPa | ASTM D638 |
| 23°C | 5000 - 12500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 88.1 - 111 | MPa | ASTM D638 |
| Yield, 23°C | 98.9 - 125 | MPa | ISO 527-2 |
| Fracture, 23°C | 94.8 - 111 | MPa | ASTM D638 |
| 23°C | 75.4 - 125 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.4 - 1.5 | % | ASTM D638 |
| Fracture, 23°C | 1.9 - 3.0 | % | ASTM D638 |
| Fracture, 23°C | 2.0 - 2.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 4440 - 12800 | MPa | ASTM D790 |
| 23°C | 5200 - 11100 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 115 - 174 | MPa | ASTM D790 |
| 23°C | 139 - 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.9 - 5.4 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 5.0 - 10 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 26 - 61 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 210 - 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 102 - 112 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 101 - 105 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 95.6 - 111 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 97.6 - 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 105 - 111 | °C | ASTM D1525 |
| -- | 105 - 115 | °C | ISO 306 |
| CLTE - Flow | 1.5E-5 - 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 9.8E+15 - 1.0E+16 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.9 - 82.5 | °C | |
| Drying Time | 2.0 - 3.5 | hr | |
| Rear Temperature | 200 - 260 | °C | |
| Middle Temperature | 220 - 260 | °C | |
| Front Temperature | 225 - 282 | °C | |
| Processing (Melt) Temp | 239 - 260 | °C | |
| Mold Temperature | 58.3 - 70.6 | °C | |
| Injection Pressure | 85.9 - 86.4 | MPa | |
| Back Pressure | 0.150 - 15.0 | MPa | |
| Screw Speed | 45 - 90 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic SAN - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENYL ZG307 - 7761 | AD majoris | Nylon 66/6 | VENYL |
| ALTECH® PA6 A 2030/606 GF30 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Plaslube® NY-1/MS/5 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| MACOMASS PP MM-PP TV 30 | MACOMASS Verkaufs AG | PP, Unspecified | MACOMASS PP |
| SECCO K7926 | Shanghai SECCO Petrochemical Co., Ltd | PP Copolymer | SECCO |