Capilene® QB 79 P
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Capilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uR6GVh_Capilene-QB-79-P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CAPILENE ® QB 79 P is a high molecular weight, low melt flow rate polypropylene random copolymer, especially designed for extrusion of pressure pipes (PP-R) and injection molding of fittings. CAPILENE ® QB 79 P features: easy processability, excellent mechanical properties, long term heat stabilization and good resistance to extraction by hot water and detergents. CAPILENE ® QB 79 P is suitable for: in-house hot and cold water pipes and fittings, floor and wall heating systems, radiator connections and industrial applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 190°C/5.0 kg | 0.50 | g/10 min | |
| 230°C/2.16 kg | 0.28 | g/10 min | |
| 230°C/5.0 kg | 1.2 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 23.0 | MPa | ASTM D638 |
| Yield | 23.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 13 | % | ASTM D638 |
| Yield | 13 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 950 | MPa | ASTM D790 |
| -- 3 | 800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 2.0 | kJ/m² | |
| 0°C | 3.5 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| 0°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | ASTM D256 | ||
| 0°C | 85 | J/m | |
| 23°C | 300 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 133 | °C | ISO 306/A, ASTM D1525 4 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polyethylene E204-01 | RheTech, Inc. | HDPE | RheTech Polyethylene |
| Sylvin 8813-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nymax™ GF 1200 A 55 HS Natural | PolyOne Corporation | Nylon 66 | Nymax™ |
| Fenochem C 3500 | Chemiplastica, Inc. | Phenolic | Fenochem |
| Generic Polyolefin, Unspecified - Glass Fiber | Generic | Polyolefin, Unspecified | Generic |