Latamid 66 B G/20-V
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uQfLrU_Latamid-66-B-G-20-V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 66 (PA 66). High fluidity. Glass fibres. Flame retardant, non classifiable. Product UL certified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.70 to 1.0 | % | |
| Flow : 2.00 mm | 0.25 to 0.45 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 8100 | MPa | |
| 60°C | 5800 | MPa | |
| 90°C | 4000 | MPa | |
| 120°C | 3200 | MPa | |
| 150°C | 2400 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 60°C | 75.0 | MPa | |
| Yield, 90°C | 60.0 | MPa | |
| Yield, 120°C | 50.0 | MPa | |
| Yield, 150°C | 45.0 | MPa | |
| Break, 23°C | 115 | MPa | |
| Break, 60°C | 75.0 | MPa | |
| Break, 90°C | 60.0 | MPa | |
| Break, 120°C | 50.0 | MPa | |
| Break, 150°C | 40.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 60°C | 3.0 | % | |
| Yield, 90°C | 4.5 | % | |
| Yield, 120°C | 4.8 | % | |
| Yield, 150°C | 6.0 | % | |
| Break, 23°C | 2.5 | % | |
| Break, 60°C | 4.0 | % | |
| Break, 90°C | 5.0 | % | |
| Break, 120°C | 5.0 | % | |
| Break, 150°C | 6.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.8 | kJ/m² | |
| 23°C | 3.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 25 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Notched Izod Impact | ASTM D256A | ||
| -20°C, 3.20 mm | 30 | J/m | |
| 23°C, 3.20 mm | 40 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 235 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 90.0 | °C | |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Oxygen Index | 33 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP HG3101 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Stanyl® TS350 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Estane® 2355-95AE TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| Kepital® LX-30 BK | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Plasmer 1050DBC/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |