| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uQQgym_SCHULAMID-66GF25.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| Nylon 66 25% Glass Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Viscosity Number | 140 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 150 | MPa | ISO 527-2/5 |
| Flexural Modulus 1 | 7800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 9.5 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | °C | ISO 75-2/A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 25 | % | ASTM D5630 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 136F6Q32 | SAX Polymers | Nylon 6 | SAXAMID™ |
| CONATHANE庐 EN-16 | Cytec Industries Inc. | PUR, Unspecified | CONATHANE® |
| Kumho KNB 3430G | Korea Kumho Petrochemical Co., Ltd. | NBR | Kumho KNB |
| Hostacom M4 N01 LW92341 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Sylvin 3230-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |