SCHULAKETON HV 4DE
| Category: | PK-Aliphatic , Polyketone, Aliphatic |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAKETON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uQGGoG_SCHULAKETONHV4DE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High viscosity aliphatic Polyketon, flame-retardant, halogen free |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (240°C/2.16 kg) | 5.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2050 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 35 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 2350 | MPa | ISO 178 |
| Flexural Stress 2(3.5% Strain) | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | |||
| -30°C | 80 | kJ/m² | ISO 179 |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 178 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 112 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 214 | °C | ISO 306/A50 |
| -- | 184 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.40 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 0.8 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 1.6 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 3.2 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.75 mm | 960 | °C | IEC 60695-2-12 |
| 1.5 mm | 960 | °C | IEC 60695-2-12 |
| 3.0 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.75 mm | 825 | °C | IEC 60695-2-13 |
| 1.5 mm | 825 | °C | IEC 60695-2-13 |
| 3.0 mm | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 33 | % | ISO 4589-2 |
| Additional Information |
|---|
| 1.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 1030EU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced TPO | POLYTROPE® |
| Sindustris PC HI5003A | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Moplen EP548R | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Sylvin 8225-80 Brown 7436 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 3712 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |