WPP PP PPH2GF3-Black
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uQ41Wo_WPP-PP-PPH2GF3-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP PP PPH2GF3-Black is a polypropylene homopolymer (PP Homopoly) product, which contains a 30% glass fiber reinforced material. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. WPP PPH2GF3-Black applications include the automotive industry and consumer goods. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 75.0 | MPa | ISO 527-2/50 |
| Fracture 1 | 78.0 | MPa | ASTM D638 |
| Fracture | 78.0 | MPa | ISO 527-2 |
| Fracture | 88.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 6.5 | % | ISO 527-2/50 |
| Fracture 2 | 6.0 | % | ASTM D638 |
| Fracture | 6.5 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 3 | 5100 | MPa | ASTM D790 |
| -- 4 | 5400 | MPa | ISO 178 |
| Flexural Stress 5 | 118 | MPa | ISO 178 |
| Ultimate Tensile Strength 6 | 80.0 | MPa | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 43 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 95 | J/m | ASTM D256 |
| -40°C | 6.5 | kJ/m² | ISO 180 |
| 23°C | 9.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 600 | J/m | ASTM D256 |
| 23°C | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 156 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 148 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 146 | °C | ISO 75-2/A |
| 1.8 MPa, not annealed | 141 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 161 | °C | ASTM D1525 |
| Additional Information |
|---|
| Material is tested at 73 ± 3°F and 50 ± 5% Relative Humidity unless otherwise noted. |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 5 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Proteus® Natural PPH | Quadrant Engineering Plastic Products | PP Homopolymer | Quadrant EPP |
| Daelim Po1y® PP-184 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| Sylvin 9604-90-LMW-CLEAR 896 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9067-70 White 1244 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® BKV 60 XF 900116 | LANXESS GmbH | Nylon 6 | Durethan® |