LNP™ LUBRICOMP™ DFL36ELH compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uPd7ek_LNP-LUBRICOMP-DFL36ELH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DFL36ELH is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractable, Easy Molding, Healthcare. Also known as: LNP* LUBRICOMP* Compound DFL-4036 EM LE HC Product reorder name: DFL36ELH |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.71 | % | ISO 294-4 |
| Flow : 24 hr | 0.21 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9650 | MPa | ASTM D638 |
| -- | 9280 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 114 | MPa | ASTM D638, ISO 527-2 |
| Break | 112 | MPa | ASTM D638 |
| Break | 113 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.4 | % | ASTM D638 |
| Yield | 2.5 | % | ISO 527-2 |
| Break | 2.5 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8960 | MPa | ASTM D790 |
| -- | 8700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 179 | MPa | ASTM D790 |
| -- | 180 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.58 | ||
| vs. Itself - Static | 0.50 | ||
| Wear Factor - Washer | 27.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 180 | J/m | ASTM D256 |
| 23°C 2 | 17 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 850 | J/m | ASTM D4812 |
| 23°C 3 | 52 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 21.8 | J | ASTM D3763 |
| -- | 7.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 147 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 149 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 143 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 144 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 4.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® AMV TL | Arkema | Nylon 12 | Rilsan® |
| PTFA 25 | Polymer Tailoring Ltd. | Polyolefin, Unspecified | PTFA |
| TOYOBO Urethane E2080A | TOYOBO America, Inc. | PUR-Capro | TOYOBO Urethane |
| Ad-Tech Epoxy EC-417 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| CYCOLAC™ INP362 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |