LNP™ LUBRICOMP™ DFP36 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uPBKfo_LNP-LUBRICOMP-DFP36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DFP36 is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DFL-4536 Product reorder name: DFP36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow (24 hr) | 3.0E-3 to 5.0E-3 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.080 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8710 | MPa | ISO 527-2/1 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.0 | ||
| vs. Itself - Static | 0.0 | ||
| Flexural Strain at Break 1 | 0.0 | % | ISO 178 |
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.00 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 0.00 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 180 | J/m | ASTM D256 |
| 23°C 2 | 17 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 740 | J/m | ASTM D4812 |
| 23°C 3 | 49 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 7.32 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 146 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 144 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4000 AF-1115 V0 | RTP Company | PPA | RTP |
| Colorite 66 Series 7566 | Colorite Polymers | PVC, Unspecified | Colorite 66 Series |
| DeWAL DW 402 | DeWAL Industries | UHMWPE | DeWAL |
| Plaslube® AC-80/TF/10 | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |
| NHU-PPA N200 | Zhejiang NHU Comp. Ltd. | PPA | NHU-PPA |