LNP™ STAT-KON™ RE003 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uOaT4c_LNP-STAT-KON-RE003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* RE003 is a compound based on Nylon 66 resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound RC-1003 Product reorder name: RE003 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 to 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.68 to 0.78 | % | ISO 294-4 |
| Flow : 24 hr | 0.17 to 0.26 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.93 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11700 | MPa | ASTM D638 |
| -- | 11600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 201 | MPa | ASTM D638 |
| Break | 180 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.6 | % | ASTM D638 |
| Break | 2.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 11300 | MPa | ASTM D790 |
| -- | 10700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 302 | MPa | ASTM D790 |
| -- | 288 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 65 | J/m | ASTM D256 |
| 23°C 2 | 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| 23°C 3 | 43 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.54 | J | ASTM D3763 |
| -- | 2.60 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 260 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 250 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 250 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 261 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.9E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safron® H106-02NSA | Safripol (PTY) LTD | PP Homopolymer | Safron® |
| Nymax™ XGF 1200A 55 HS UV BLACK | PolyOne Corporation | Nylon 66 | Nymax™ |
| DELPET™ SR6500 | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |
| Flexathene® TP4346HS | LyondellBasell Industries | Polyolefin, Unspecified | Flexathene® |
| CP PRYME® ABS A100-36 | Chase Plastics Services Inc. | ABS | CP PRYME® ABS |