TOTAL Polyethylene Lumicene® M 2735
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uONwUc_TOTAL-Polyethylene-Lumicene-M-2735.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lumicene® mPE M 2735 S01 is a Lumicene® metallocene based Polyethylene with hexene as comonomer. Lumicene® mPE M 2735 S01 can be processed at high output rates with low extrusion pressure, low neck-in, excellent drawability and good gauge control. Together with these features, Lumicene® mPE M 2735 S01 ensures films with outstanding optical properties and excellent impact and tear resistance. Lumicene® mPE M 2735 S01 is suited for many applications in the field of cast film, stretch wrap film (low cling), hygiene film (f.e. diaper backsheet), lamination and artificial grass. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.927 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm, cast film | 9.00 | MPa | ISO 527-3 |
| TD : Yield, 20 µm, cast film | 9.00 | MPa | ISO 527-3 |
| MD : Fracture, 20 µm, cast film | 39.0 | MPa | ISO 527-3 |
| TD : Fracture, 20 µm, cast film | 24.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 20 µm, cast film | 470 | % | ISO 527-3 |
| TD : Fracture, 20 µm, cast film | 530 | % | ISO 527-3 |
| Dart Drop Impact (20 µm, Cast Film) | 130 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 20.0 µm | 50.0 | kN/m | ISO 6383-2 |
| TD : 20.0 µm | 120.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 118 | °C | ISO 306 |
| Melting Temperature | 119 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm, Cast Film) | 89 | ASTM D2457 | |
| Haze (20.0 µm, Cast Film) | 1.3 | % | ISO 14782 |
| Additional Information |
|---|
| Film data obtained using laboratory test specimens produced with the following extrusion conditions: Die Gap = 250 µm, Chill Roll Temperature: 20°C, Throughput = 7 kg/h, Melt Temperature: 260°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 240 - 280 | °C | |
| Take-Off Roll | 20.0 - 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PVC BOTTLE GRADE K57 | Marco Polo International, Inc. | PVC, Rigid | MARPOL® PVC |
| MARPOL® COPP 17.NB | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |
| KUBE PIR 40253 | KUBE Electronics AG | HDPE | KUBE PIR |
| Iupilon® GSH2020DF | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LNP™ THERMOCOMP™ RX00713H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |