Karina IVORY PVC COMPOUND 90540-35/1-Y-IS-SD
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uO4HYF_Karina-IVORY-PVC-COMPOUND-90540-35-1-Y-IS-SD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FLAME RETARDANT PVC COMPOUND RECOMMENDED FOR THIN WALL INSULATION OF AUTOMOTIVE ELECTRICAL WIRES FOR WORKING AT THE TEMPERATURE RANGE OF - 20C TO 105C. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.27 to 1.33 | g/cm³ | ASTM D792 |
| Color | 0.00OK | ME 12 | |
| Color a | -1.66 to 1.34 | ME 12 | |
| Color b | 4.56 to 7.56 | ME 12 | |
| Color L | 89.7 to 92.7 | ME 12 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 46 to 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 14.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 150 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 0.00 | MPa | NBR 9148 |
| Tensile Elongation 3(Break) | > 0.0 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 3.0E+14 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Faraprene 200 | Primex Plastics Corporation | TPE Alloy | Prime Faraprene |
| ColorFast® PBT100 | LTL Color Compounders, Inc. | PBT | ColorFast® |
| DOW™ Electrical & Telecommunications DFDA-1254 NT | The Dow Chemical Company | LDPE | DOW™ Electrical & Telecommunications |
| HI-ZEX™ 630ET | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| LNP™ LUBRICOMP™ ZP001XXP compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |