T & T Marketing TPE 6187
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | T & T Marketing, Inc. |
| Trademark: | T & T Marketing |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uNNRZf_T-T-Marketing-TPE-6187.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TPE 6187 is a natural, thermoplastic elastomer (TPV) intended for wire and cable insulation and jacketing. It is designed to offer excellent low temperature flexibility and deformation resistance. TPE 6187 offers good extrusion processing characteristics on either conventional polyethylene or PVC extrusion lines. TPE 6187 is readily pigmented to a variety of colors using standard wire and cable color concentrates designed for thermoplastic or crosslinked polyolefins. UV weather resistance is obtainable by the addition of a suitable carbon black or UV additive. Application TPE 6187 is intended for pump cable, flexible cord insulation, and fixture applications. (It is also suitable for use in wet locations.) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.970 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 0.762 mm) | 83 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (0.762 mm) | 15.2 | MPa | ASTM D412 |
| Tensile Elongation (Break, 0.762 mm) | 800 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Retention of Tensile Elongation - 7 days at 136°C (762.0 µm) | > 65 | % | UL 1581 |
| Retention of Tensile Strength - 7 days at 136°C (762.0 µm) | > 85 | % | UL 1581 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deformation (150°C, 762.0 µm) | < 20 | % | UL 1581 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extruder Screw Compression Ratio | 3:1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -45.6 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.91 mm) | 26 | kV/mm | ASTM D149 |
| Dielectric Constant (1.91 mm, 60 Hz) | 2.20 | ASTM D150 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 185 | °C | |
| Cylinder Zone 2 Temp. | 193 | °C | |
| Cylinder Zone 3 Temp. | 202 | °C | |
| Cylinder Zone 4 Temp. | 213 | °C | |
| Melt Temperature | 213 to 218 | °C | |
| Die Temperature | 216 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ A700 G30 H | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Celstran® PP-GF30-0405 P10/16 | Celanese Corporation | PP, Unspecified | Celstran® |
| MAJORIS GFR400 | AD majoris | PP, Unspecified | MAJORIS |
| OXNILON 6 4IMP | Oxford Polymers | Nylon 6 | OXNILON 6 |
| POCAN® C 1202 000000 | LANXESS Asia/Pacific | PC+PBT | POCAN® |