TOTAL Polyethylene HDPE HP 401 N
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uN1GS1_TOTAL-Polyethylene-HDPE-HP-401-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Polyethylene HP 401 N is a high density (HMW) polyethylene material,. This product is available in North America or Asia Pacific region. The processing method is: pipeline extrusion molding. The main features of TOTAL Polyethylene HP 401 N are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.945 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.080 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 8.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, F0) | > 1000 | hr | ASTM D1693C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 22.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 800 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 862 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 590 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 126 | °C | ASTM D3418 |
| Additional Information |
|---|
| Cell Classification, ASTM D3350: 345464Elongation at Break, ASTM D638, Type IV, 2 in/min: >800%Hydrostatic Design Basis, ASTM D2837, 140°F: 800 psiHydrostatic Design Basis, ASTM D2837, 73°F: 1600 psiPENT, ASTM F1473: >100 hrsPPI Recommended Designation: PE 3608, PE 3408Tensile Strength at Yield, ASTM D638, Type IV, 2 in/min: >3300 psi |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 191 - 221 | °C | |
| Cylinder Zone 2 Temp. | 191 - 221 | °C | |
| Cylinder Zone 3 Temp. | 191 - 221 | °C | |
| Cylinder Zone 4 Temp. | 191 - 221 | °C | |
| Cylinder Zone 5 Temp. | 191 - 221 | °C | |
| Melt Temperature | 210 | °C |
| Extrusion instructions |
|---|
| Vacuum Tank Water Temperature: 73°F |
| Note Message | |
|---|---|
| 1 . | Type 4, 51mm/min |
| 2 . | Type 4, 51mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® CP-28126 | Teknor Apex Company | TPE | Monprene® |
| VINIKA® CF50FA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| DIOSHY® TPO F990-OS | DIOSHY Co.,Ltd. | TPO (POE) | DIOSHY® |
| Shida 2500 | JINJIANG City SHIDA Plastic Fine Co., Ltd. | TPE | Shida |
| POCAN® B 3235 POS151 000000 | LANXESS GmbH | PBT | POCAN® |