HiPrene® HSG43BE
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | GS Caltex |
| Trademark: | HiPrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uLKF5D_HiPrene-HSG43BE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiPrene® HSG43BE is a glass fiber filled poylpropylene compound suitable for injection moulding. This material combines good stiffness, good processability and surface finish. It has been developed for Industrial Parts and Non-visible Automotive Parts. This material is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 3.5 | g/10 min | ISO 1133 |
| Ash Content (600°C) | 30 | % | ISO 3451 |
| Volatile Matter | 0.10 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 106 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 95.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.5 | % | ISO 527-2 |
| Flexural Modulus 1(23°C) | 6000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179/1eA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 4.00 - 6.50 | MPa |
| Injection instructions |
|---|
| Back Pressure: Low to MediumScrew Speed: Low to MediumInjection Speed: 100 to 200 m/min |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2500N0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Axiall PVC 8540 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Ebalta MG 804 / Comp. A+B | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| KOPLA PA66 KDG1030 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| LEXAN™ ML2010 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |