Elastollan® 560 A 13 PTSG 000
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uLA2DP_Elastollan560A13PTSG000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Polyester-Polyurethane with excellent mechanical properties and a high abrasion resistance. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 3 sec) | 60 | DIN 7619-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 90.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504-S2 | ||
| 20% strain | 1.00 | MPa | DIN 53504-S2 |
| 100% strain | 2.50 | MPa | DIN 53504-S2 |
| 300% strain | 6.00 | MPa | DIN 53504-S2 |
| Tensile Stress (Yield) | 24.0 | MPa | DIN 53504-S2 |
| Tensile Elongation (Break) | 850 | % | DIN 53504-S2 |
| Tear Strength 1 | 50 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 29 | % | ISO 815 |
| 70°C, 24 hr | 45 | % | ISO 815 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40 | °C | |
| Rear Temperature | 195 - 205 | °C | |
| Middle Temperature | 200 - 210 | °C | |
| Front Temperature | 200 - 210 | °C | |
| Nozzle Temperature | 205 - 215 | °C | |
| Processing (Melt) Temp | 200 - 210 | °C | |
| Mold Temperature | 20 - 40 | °C | |
| Injection Rate | Slow | ||
| Back Pressure | 5.00 - 15.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 137777 C | RTP Company | PP, Unspecified | RTP |
| SABIC® LLDPE 6118NSF | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| SAMAT 5003A | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| 3M™ Dyneon™ Fluoroelastomer FC 2123Z | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| LUVOCOM® 1-7321-5 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |