Estane® 5714 TPU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uIVXIg_Estane-5714-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Type: Estane® 5714 is a Polyether Type Thermoplastic Polyurethane (TPU). Features: Low Temperature Flexibility, Excellent Abrasion, Fungal, and Chemical Resistance, and Hydrolytic Stability. Adhesives can be applied from solution or extruded as a melt coating. The resin is lightly dusted with calcium stearate and contains UV stabilizer. Uses: Various adhesive and fabric coating, magnetic media binder and cast films for lamination |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 31.0 | MPa | |
| 100% Strain | 4.80 | MPa | |
| 300% Strain | 9.00 | MPa | |
| Tensile Elongation (Break, 0.762 mm) | 530 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 4.80 | MPa | |
| 300% Strain | 9.00 | MPa | |
| Tensile Strength (Break) | 31.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 530 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -38.0 | °C | DSC |
| Vicat Softening Temperature | 71.0 | °C | ASTM D1525 |
| Ring and Ball Softening Point | 174 | °C | ASTM E28-92 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brookfield Viscosity 1 | |||
| 15% T.S. in Cyclohexanone : 23°C | 3.70 | Pa·s | |
| 15% T.S. in THF : 23°C | 0.900 | Pa·s |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gradient Bar Tack Temperature | 127 | °C | |
| Open Time | < 5.0 | sec | ASTM D4497-94 |
| T-Peel | ASTM D1876 | ||
| Aluminum Foil | 500.0 | N/m | |
| Mylar Film | 1500.0 | N/m |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (204°C) | 72.0 | Pa·s | ASTM D1084 |
| Note Message | |
|---|---|
| 1 . | RVT Spindle #2, 20 RPM |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viprene™ P65A-22U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| Trexprene® A80BW | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| NILAMID® A3 AL40 | Nilit Plastics | Nylon 66 | NILAMID® |
| Sylvin 6930X06 Brown 7483 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| StarMed® 9055-1007 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarMed® |