InnoPlus LL9641U
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uINgd3_InnoPlus-LL9641U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
InnoPlus LL9641U/LL9641UP are hexene co-polymer based linear low density polyethylene which are designed for rotational molding applications. These are UV-stabilized rotational molding grades which provide an excellent stiffness and a good balance between impact strength and environmental stress cracking resistance. InnoPlus LL9641UP is a powder form of InnoPlus LL9641U. InnoPlus LL9641U/LL9641UP can be used to produce variety applications such as general molding, toys & playground equipments, outdoor storage containers, medium to large water tanks and chemical tanks. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.939 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 1.90 mm, 100% Igepal, Compression Molded, F50) | 100 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 57 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 20.0 | MPa | |
| Break, Compression Molded | 25.0 | MPa | |
| Tensile Elongation (Break, Compression Molded) | 950 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 750 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1(Compression Molded) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 118 | °C | ASTM D1525 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Oven Temperature | 260 to 290 | °C |
| Note Message | |
|---|---|
| 1 . | Partial Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 204 GB FR | RTP Company | Nylon 66 | RTP |
| S&E Wire & Cable GTPE-2203G1 | S&E Specialty Polymers, LLC | TPE | S&E Wire & Cable |
| Taitacell EPS-361T | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Chemical Resources PP 200 | Chemical Resources, Inc. | PP Homopolymer | Chemical Resources |
| Petrothene® NA205000X01 | LyondellBasell Industries | LDPE | Petrothene® |