LNP™ THERMOCOMP™ ZF0089 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uIHZiM_LNP-THERMOCOMP-ZF0089-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP ZF0089 is a compound based on PPO resin containing 40% Glass Fiber. Added features of this material include: Exceptional Processing, Flame Retardant. Also known as: LNP* THERMOCOMP* Compound ZF-1008 EP FR Product reorder name: ZF0089 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.52 | g/cm³ | ASTM D792 |
| -- | 1.51 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.50 | % | |
| Across Flow : 24 hr | 0.50 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.070 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.090 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13000 | MPa | ASTM D638 |
| -- | 12300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 101 | MPa | ASTM D638 |
| Break | 8.00 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.1 | % | ASTM D638 |
| Break | 0.88 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 11800 | MPa | ASTM D790 |
| -- 5 | 11900 | MPa | ISO 178 |
| Flexural Strength 6(Break, 50.0 mm Span) | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 74 | J/m | ASTM D256 |
| 23°C 7 | 6.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 330 | J/m | ASTM D4812 |
| 23°C 8 | 20 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 12.3 | J | ASTM D3763 |
| -- | 3.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 110 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 112 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 103 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 105 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 to 288 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 299 to 310 | °C | |
| Processing (Melt) Temp | 299 to 304 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP HI5205G | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Ultramid® A3W R01 SW805 | BASF Corporation | Nylon 66 | Ultramid® |
| Aarolene® ARPS HI 100-4 | Aaron Industries Corp. | PS (HIPS) | Aarolene® |
| ELASTOSIL® R 500/60 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| IROGRAN® A 85 H 4827 | Huntsman Corporation | TPU-Polyester | IROGRAN® |