Ultramid® BG50XFI
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uGzkE2_Ultramid-BG50XFI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid BG50XFI is an impact modified, injection molding type 6 nylon graft copolymer with superior impact resistance and flow especially for thinner walled parts and long flow lengths. It is also available in natural and pigmented versions. Copolymerization results in varying levels of toughness and flexibility combined with excellent thermal and chemical properties. Exhibits higher impact performance than that of conventional nylon homopolymers while maintaining good strength, chemical resistance and stiffness. Applications Ultramid BG50XFI is generally recommended for applications such as cellular phone housings, handheld device, caps, furniture rails, covers, mower decks and tool. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.10 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption | ||||
| Saturation | 8.6 | -- | % | ASTM D570 |
| Saturation, 23°C | 8.6 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.4 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2500 | 755 | MPa | ISO 527-2 |
| Tensile Strength (Yield, 23°C) | 70.0 | 36.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | ||||
| Yield, 23°C | 4.0 | 28 | % | ASTM D638, ISO 527-2 |
| Break, 23°C | 70 | > 100 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | > 50 | > 50 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 2390 | -- | MPa | ASTM D790 |
| 23°C | 2350 | 670 | MPa | ISO 178 |
| Flexural Strength | ||||
| 23°C | 95.0 | -- | MPa | ASTM D790 |
| 23°C | 85.0 | 20.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ||||
| 23°C | 150 | -- | J/m | ASTM D256 |
| 23°C | 15 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 57.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| RTI Elec | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Drop Weight Impact Strength (23°C) | 201 | -- | J | Internal Method |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 285 | °C | |
| Mold Temperature | 65.0 to 80.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL TP-HG15 | Polymer Resources Ltd. | PBT | PRL |
| SEPTON™ 2004 | Kuraray Co., Ltd. | SEPS | SEPTON™ |
| APEX® 78-A447R-21 | Teknor Apex Company | PVC, Flexible | APEX® |
| DOWLEX™ 2645.11S | The Dow Chemical Company | LLDPE | DOWLEX™ |
| Moplen HP504N | LyondellBasell Industries | PP Homopolymer | Moplen |