A single component, UV curable, thixotropic flexible epoxy adhesive/encapsulant designed for semiconductor and opto-electronic packaging. Glob top over IC and wire bonds, and low stress bonding of fiber optic components, are common applications. It is a replacement for EPO-TEK® OG133-5, and a non-flow version of EPO-TEK® OG133-7. Formerly 90-36-4 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 10.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 353 | °C | |
| Operating Temperature | |||
| Continuous | -55 to 150 | °C | |
| Intermittent | -55 to 250 | °C | |
| Storage Modulus | < 6.89 | MPa | |
| Thixotropic Index | 3.10 | ||
| Weight Loss on Heating | |||
| 200°C | 2.4 | % | |
| 250°C | 3.6 | % | |
| 300°C | 5.7 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | < 10.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 4.3E-5 | cm/cm/°C | |
| -- 3 | 2.2E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index | |||
| -- 4 | 1.504 | ||
| -- 5 | 1.524 | ||
| Transmittance | |||
| 640 nm | > 90.0 | % | |
| 900 nm | > 95.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | White | ||
| Density | 1.13 | g/cm³ | |
| Viscosity 6(23°C) | 1.0 to 1.5 | Pa·s |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore A) | 65 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm (uncured) |
| 5 . | 589 nm (cured) |
| 6 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9886-90 BLACK 244 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Bormed™ LE6607-PH | Borealis AG | LDPE | Bormed™ |
| Lion Idemitsu Composites PPS Y551F1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| LNP™ LUBRILOY™ D2000P compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |
| Lucon® PO6062 | LG Chem Ltd. | PPE+PS | Lucon® |