VALOX™ 457 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uGMmYg_VALOX-457-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 6.5% GR PBT, UL94 V-0/5V. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Specific Volume | 0.690 | cm³/g | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.60 to 0.80 | % | |
| Flow 2 | 0.80 to 1.0 | % | |
| Across Flow 3 | 0.70 to 0.90 | % | |
| Across Flow 4 | 0.90 to 1.2 | % | |
| Water Absorption (24 hr) | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 5(Break) | 79.3 | MPa | ASTM D638 |
| Flexural Modulus 6(50.0 mm Span) | 3520 | MPa | ASTM D790 |
| Flexural Strength 7(Break, 50.0 mm Span) | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 270 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 204 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 152 | °C | |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow | ASTM E831 | ||
| -40 to 40°C | 6.7E-5 | cm/cm/°C | |
| 60 to 138°C | 6.7E-5 | cm/cm/°C | |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 5.5E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Oil | 24 | kV/mm | |
| 3.20 mm, in Air | 18 | kV/mm | |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 3.50 | ||
| 1 MHz | 3.40 | ||
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 2.0E-3 | ||
| 1 MHz | 0.020 | ||
| Arc Resistance 8 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.711 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 3.00 mm 9 | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 750 | °C | |
| 3.00 mm | 725 | °C | |
| Oxygen Index | 32 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 1.5 to 3.2 mm |
| 2 . | 3.2 to 4.6 mm |
| 3 . | 1.5 to 3.2 mm |
| 4 . | 3.2-4.6 mm |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | Tungsten Electrode |
| 9 . | by VDE |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SNOLEN® EF 2.1/46 S | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| UNISOFT TPE™ ST-90A-NT-4-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| Canuck Compounds 100 Series - BK 1-4-0 | Canuck Compounders Inc. | PE, Unspecified | Canuck Compounds |
| Hifax EYS 145P Black | LyondellBasell Industries | PP Copolymer | Hifax |
| LNP™ LUBRICOMP™ Lexan_LF1510A compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |