3M™ Dyneon™ Fluoroelastomer FE 5620N

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	uGKWQD_3MDyneonFluoroelastomerFE5620N.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
3M™ Dyneon™ Fluoroelastomer FE 5620N is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FE 5620N has an incorporated bisphenol cure system. Special Features Composition: dipolymer of vinylidene fluoride and hexafluoropropylene Process targets: injection and transfer moulding, extrusion and calendering Proprietary incorporated cure technology Improved cure technology resulting in more consistent part size from successive moulding cycles Low viscosity version of 3M™ Dyneon™ Fluoroelastomer FE 5640Q Improved scorch resistance at high moulding temperatures Excellent mould release - can be used in automated injection moulding equipment Clean running Compounds prepared from Dyneon FE 5620N can be formulated to meet Mil-R-83248 Typical Applications 3M™ Dyneon™ Fluoroelastomer FE 5620N is suitable to produce O-rings in an injection moulding process.

Message

3M™ Dyneon™ Fluoroelastomer FE 5620N is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FE 5620N has an incorporated bisphenol cure system.

Special Features

Composition: dipolymer of vinylidene fluoride and hexafluoropropylene

Process targets: injection and transfer moulding, extrusion and calendering

Proprietary incorporated cure technology

Improved cure technology resulting in more consistent part size from successive moulding cycles

Low viscosity version of 3M™ Dyneon™ Fluoroelastomer FE 5640Q

Improved scorch resistance at high moulding temperatures

Excellent mould release - can be used in automated injection moulding equipment

Clean running

Compounds prepared from Dyneon FE 5620N can be formulated to meet Mil-R-83248

Typical Applications
3M™ Dyneon™ Fluoroelastomer FE 5620N is suitable to produce O-rings in an injection moulding process.

General Information
Features	Low viscosity Good demoulding performance
Uses	O-rings
Agency Ratings	MIL R-83248
Appearance	Opacity White-like
Forms	Thick sheet
Processing Method	Extrusion Resin transfer molding Calendering Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.80	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	23	MU	Internal method
Fluorine Content	66	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	77		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	6.00	MPa	ASTM D412A
Tensile Strength ²	16.5	MPa	ASTM D412A
Tensile Elongation ³(Break)	210	%	ASTM D412A
Compression Set			ASTM D1414
200°C, 70 hr ⁴	14	%	ASTM D1414
200°C, 70 hr ⁵	12	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould
4 .	Post cured 16 hours @ 230°C
5 .	Post cured 24 hours @ 260°C

Resin Grade	Manufacturer	Category	Trademark
Marlex® PP HGZ-120SP	Saudi Polymers Company	PP Homopolymer	Marlex® PP
EMLON® 66 GFR 30	EMAS Plastik San.Tic.AS.	Nylon 66	EMLON®
Sylvin 802-88 Green 3185	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Tunhe PBT TH6095	Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd	PBT	Tunhe PBT
Comco PA6G FOOD	Comco Nylon GmbH	Nylon 6	Comco