EL-Lene™ H511W
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uGFl7K_EL-Lene-H511W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Lene H511W is a high density polyethylene for solid insulation in cable application. It is also suitable for outer skin in "foam skin" constructions. It provides good performance across the full range of tele-communication insulation applications, including aircore and petroleum jelly filled cable designs in both buried and aerial environments. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 10% Igepal, F0) | > 168 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 23.0 | MPa | |
| Break | 34.0 | MPa | |
| Tensile Elongation 2(Break) | > 600 | % | ASTM D638 |
| Flexural Modulus | > 800 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Oxidation Induction Time (200°C) | > 100 | min | ASTM D3895 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.32 | ASTM D1531 | |
| Dissipation Factor (1 MHz) | 6.0E-5 | ASTM D1531 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 to 280 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ Fluoroelastomer FT 2430 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| HiFill® PA6 0177 B | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| LUVOCOM® 1105-7876-1 VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| SQUARE® SCR2524-70A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| Sylvin 29168-75 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |