Crastin® FR1300TC BK350
| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Crastin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uGF8fB_CrastinFR1300TCBK350.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermally Conductive, Flame Retardant, Polybutylene Terephthalate |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.60 | % | ISO 294-4 |
| Flow | 0.40 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 34.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2 |
| Flexural Modulus | 6600 | MPa | ISO 178 |
| Flexural Stress | 51.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 6.8 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 195 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 119 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 4.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 5.3E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | ASTM E1461 | ||
| -- 1 | 2.0 | W/m/K | ASTM E1461 |
| -- 2 | 14 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 3 | 1.0E+5 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.75 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| FMVSS Flammability | DNI | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 275 | °C | |
| Mold Temperature, Optimum | 110 | °C | |
| Back Pressure | As low as possible | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Ejection Temperature | 170 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Max Regrind | 15 | % | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 100 - 120 | °C | |
| Holding Pressure | 60.0 | MPa |
| Note Message | |
|---|---|
| 1 . | through plane |
| 2 . | in plane |
| 3 . | Assessed (Min) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2585 FR | RTP Company | PC+ABS | RTP |
| Sinvicomp SIZ4809 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| TOTAL Polystyrene 3241 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Nypol® PA A3 G10 NTLA010 NR452 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Flontech® FT-WA15-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |