MAJORIS DW100 - 8229
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uFasEy_MAJORIS-DW100---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DW100 - 8229 is a 10% glass-filled polypropylene compound intended for injection moulding. The product is available in natural (DW100), but other colours can be provided on request. The good flow ability of DW100 - 8229 makes it very easy to process even for complicated parts with long flow paths and it offers very high productivity with short cycle times. DW100 - 8229 is formulated to give an excellent surface finish. APPLICATIONS
Products requiring rigidity, shrinkage and good dimensional stability can suitably be made from DW100 - 8229. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 1.3 - 1.8 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 12 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 27 | kJ/m² | ISO 179 |
| 23°C | 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 53.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 148 | °C | ISO 306/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HMP-305U (Roto) | Ravago Manufacturing Americas, LLC | LLDPE | Ravago Compounds |
| Clariant Nylon 6 60G13-L | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| LubriOne™ PC-20CF/15T | PolyOne Corporation | PC | LubriOne™ |
| Lupoy® 1301V-10 | LG Chem Ltd. | PC | Lupoy® |
| PIVINEL™ 114-R1-LF | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |