Braskem PE SLL218
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uFU7a6_Braskem-PE-SLL218.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SLL218 is a Linear Low Density Polyethylene, copolymer of butene-1. Developed for cast film extrusion. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as processability. Very low gel amount. It contains antioxidant additives. The minimum biobased content of this grade is 87%, determined according to ASTM D6866. Applications: Stretch films; liners; LDPE and HDPE blends and packages for general use. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm, Cast Film | 40.0 | MPa | |
| TD : Break, 38 µm, Cast Film | 30.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm, Cast Film | 1300 | % | |
| TD : Break, 38 µm, Cast Film | 1600 | % | |
| Flexural Modulus | ASTM D882 | ||
| 1% Secant, MD : 38 µm, Cast Film | 200 | MPa | |
| 1% Secant, TD : 38 µm, Cast Film | 230 | MPa | |
| Dart Drop Impact 1(38 µm, Cast Film) | 100 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, Cast Film | 150 | g | |
| TD : 38 µm, Cast Film | 190 | g |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 87 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NB30 GR13 BK EF | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| WPP PP PPC3GF1.5-Natural | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| BMC 860 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Chemical Resources RPP 100CW | Chemical Resources, Inc. | PP Random Copolymer | Chemical Resources |
| Fainplast PVC CKL 87/6 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |