Kynar Flex® 2750-01

Category:	PVDF , Polyvinylidene Fluoride
Manufacturer:	Arkema
Trademark:	Kynar Flex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	uEfGmm_Kynar-Flex-2750-01.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

KYNAR FLEX® 2750-01 is a semi-crystalline VF2 based copolymer. It has been designed for applications requiring high flexibility and improved resistance to impact.

KYNAR FLEX® 2750-01 can be used in extrusion and injection molding processes.

ADDITIONAL CHARACTERISTICS:
Excellent thermal stability
Excellent abrasion resistance
Excellent purity and chemical resistance
Impervious to UV degradation
Self extinguishing material
Extremely low smoke emission characteristics
Pigmentable

KYNAR FLEX® 2751-00 is the powder version of this product.

General Information
Features	Good Abrasion Resistance Good Chemical Resistance Good Colorability Good Flexibility Good Impact Resistance Good Thermal Stability Good UV Resistance High Purity Low Smoke Emission Self Extinguishing Semi Crystalline
Forms	Pellets
Processing Method	Extrusion Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.78 to 1.82	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 23°C)	55 to 62		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield, 23°C	13.8 to 21.4	MPa
Break, 23°C	20.0 to 27.6	MPa
Tensile Elongation (Break, 23°C)	200 to 400	%	ASTM D638
Flexural Modulus (23°C)	345 to 483	MPa	ASTM D790
Flexural Strength (23°C)	13.8 to 24.1	MPa	ASTM D790
Compressive Strength (23°C)	24.1 to 31.0	MPa	ASTM D695

Thermal	Nominal Value	Unit	Test Method
Peak Melting Temperature	130 to 138	°C	ASTM D3418

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity ¹(20°C)	2.0E+14	ohms·cm	ASTM D257

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (232°C, 100 sec^-1)	2000 to 2500	Pa·s	ASTM D3835

Note Message
1 .	65% R.H.

Resin Grade	Manufacturer	Category	Trademark
RTP 1381 D TFE 13 SI 2	RTP Company	PPS	RTP
LEXAN™ PC1000R resin	SABIC Innovative Plastics	PC	LEXAN™
Karina IVORY PVC COMPOUND 880-35/1-F-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Karina GRAY PVC COMPOUND 853-18/233-DY-AC-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Sylvin 9604-95C Clear 896	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin