Order Products : sales@su-jiao.com
DOWLEX™ 2045.11S
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uEYEF9_DOWLEX204511S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | Internal method |
| Film Puncture Energy | 1.24 | J | Internal method |
| Film Puncture Force | 31.1 | N | Internal method |
| Film Puncture Resistance | 6.21 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 110 | J/cm³ | ASTM D882 |
| TD | 114 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 211 | MPa | ASTM D882 |
| 2% secant, MD | 172 | MPa | ASTM D882 |
| 1% secant, TD | 234 | MPa | ASTM D882 |
| 2% secant, TD | 189 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 13.4 | MPa | ASTM D882 |
| TD : Yield | 14.1 | MPa | ASTM D882 |
| MD : Fracture | 46.1 | MPa | ASTM D882 |
| TD : Fracture | 35.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 540 | % | ASTM D882 |
| TD : Fracture | 660 | % | ASTM D882 |
| Dart Drop Impact | 180 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 440 | g | ASTM D1922 |
| TD | 630 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 122 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 34 | ASTM D2457 | |
| Haze | 20 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 216 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：DSB II 模具间隙：70 密尔 (1.8 mm) 熔体温度：430-450°F (221-232°C) 输出：模具周长的 10 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1590 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| MOSTEN GB 608 | UNIPETROL RPA | PP Copolymer | MOSTEN |
| INSTRUC PCABSGF20MD | Infinity LTL Engineered Compounds | PC+ABS | INSTRUC |
| Hostacom TYC 727N E C12716 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Geon™ Vinyl Flexible HC28000G | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |