TORZEN® G5000HSL BK20
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | INVISTA Engineering Polymers |
| Trademark: | TORZEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uE8W43_TORZEN-G5000HSL-BK20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TORZEN® G5000HSL BK20 is a 50% glass reinforced, heat stabilized, black, PA66 resin suitable for many injection molding applications where high tensile strength and dimensional stability are needed. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 2.3 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.80 to 0.90 | % | |
| Flow : 2.00 mm | 0.20 to 0.30 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.65 | % | |
| Equilibrium, 23°C, 50% RH | 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 247 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2 |
| Flexural Modulus | 16700 | MPa | ISO 178 |
| Flexural Stress | 350 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 14 | kJ/m² | |
| 23°C | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 100 | kJ/m² | |
| 23°C | 130 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 13 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 255 | °C | ISO 75-2/A |
| Melting Temperature | 262 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 to 0.18 | % | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Back Pressure | 0.200 to 1.00 | MPa | |
| Cushion | 4.00 to 6.00 | mm | |
| Vent Depth | 7.0E-3 to 0.040 | mm | |
| Screw Speed | Low rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9398 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| SILPURAN® 6600/60 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| Adell PP RR-34 | Adell Plastics, Inc. | PP Copolymer | Adell PP |
| ALTECH® PP-H A 2030/750 GF30 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| E-Pos 558 | Epocat Nederland BV | Epoxy | E-Pos |